  1. Chloride Stress Corrosion Cracking can cause cracks that normally initiate:
    On the surface of 300 series SS
  2. Which of the following is not a factor in the Chloride Stress Corrosion Cracking?
    A) Temp
    B) Stress
    C) Pressure
    D) Material
    E) Chloride strength
    C) Pressure
    (this multiple choice question has been scrambled)
  3. Which of the following can contribute to Chloride Stress Corrosion Cracking?
    A) Dissolved hydrogen
    B) Dissolved sulfide
    C) Dissolved oxygen
    D) Dissolved nitrogen
    C) Dissolved oxygen
    (this multiple choice question has been scrambled)
  4. Heat transfer equipment can provide a way for chlorides to:
    concentrate
  5. Chloride Stress Corrosion Cracking usually occurs at a pH:
    above 2
  6. Chloride Stress Corrosion Cracking usually occurs at temps above:
    140°F
  7. Nickel alloys have the greatest susceptibility to Chloride Stress Corrosion Cracking when the nickel content is :
    between 8% to 12%
  8. Nickel is highly resistant to Chloride Stress Corrosion Cracking when the nickel content in the alloy is above:
    35%
  9. External Chloride Stress Corrosion Cracking has been caused by chloride in:
    insulation