  1. What two factors contribute to Corrosion Fatigue
    Cyclic loading & Corrosion
  2. Corrosion Fatigue often initiates at
    the bottom of a pit
  3. which of the following materials is not subjected to Corrosion Fatigue?
    A) All materials are affected by Corrosion Fatigue
    B) 300-Series stainless steel
    C) Nickel alloys
    D) Chromes
    E) C.S.
    A) All materials are affected by Corrosion Fatigue
    (this multiple choice question has been scrambled)
  4. Which of the following equipment is typically not subjected to Corrosion Fatigue?
    A) Cyclic Boilers
    B) Rotating Equipment
    C) Deaerators
    D) Furnaces
    D) Furnaces
    (this multiple choice question has been scrambled)
  5. Corrosion Fatigue cracks are most often
    transgranular
  6. Corrosion Fatigue cracks in deaerators are usually
    very tight and difficult to detect